10KV One-step Silane Cross-linkable Overhead Insulation Compound Silane XLPE Insulation Compounds

Item No.: 00635
SEJ90-1-KK (10) is one-step silane cross-linkable polyethylene overhead insulation compound for medium-low voltage cables. It is a kind of insulations for medium-low voltage overhead cables through squeeze tube mold production process.
  • ModelSEJ90-1-KK(10)
  • Brand NameEASTMAC
  • Place of OriginChina
  • PortShanghai China
  • Supply Ability1000 Tons Per Month
  • Payment TermsT/T, L/C
  • More Less
    Description
    Description

    Application: 

    SEJ90-1-KK (10) is one-step silane cross-linkable polyethylene overhead insulation compound for medium-low voltage cables. It is a kind of

    insulations for medium-low voltage overhead cables through squeeze tube mold production process. Cables working voltage is 10KV and

    below, the highest working temperature is 90℃.

    Processing Indicator
    Recommend to process with the PE extruder.

     

    Main technical data:

    Model

     

    Machine Barrel Temperature 

    Molding Temprature

     

    SEJ90-1-KK(10)

    160-200℃

     

    215-220℃

     

     

    Item

     

    Unit

     

    Technical

    requirements

     

    Density

     

    g/cm3

    0.922±0.005

    Tensile Strength

     

    MPa

    ≥13.0

    Elongation at Break

     

    %

    ≥300

    Brittle Temperature with Low Temperature

     

     

    -76

    ≤15/30

    20 Volume Resistivity

     

    Ω·m

    ≥1.0×1014

    20 Dielectric Strength,50Hz

     

    MV/m

    ≥25.0

    20 Dielectric Constant,50Hz

     

    ----

    ≤2.35

     

    Air Aging Condition

    135±2×168h

    Tensile Strength Variation After

    Aging

     

     

    %

     

    ±20

    Elongation Variation After Aging 

    %

    ±20

     

    Artificial  Weathering Aging 0- 1008h

    Tensile Strength Variation After

    Aging

     

     

    %

     

    ±30

    Elongation Variation After Aging 

    %

    ±30

     

    Artificial  Weathering Aging  504- 1008h

           Tensile Strength Variation After

            Aging

     

     

    %

     

                 ±30

    Elongation Variation After Aging 

    %

                 ±30

       