XLPE Insulation Compounds

FEJ90 Irradiation Cross-linkable Insulation Compounds XLPE Insulation Materials for Wire and Cables

Item No.: 00621
FEJ90, FEJ105, FEJ125 and FEJ150 are irradiation cross-linkable insulation compounds for wire and cables, which regards polyolefin resin as the basic raw material, and adds anti-oxidant, cross-linkable agent and modified agents and other additives. They h
  • ModelFEJ90
  • Brand NameEASTMAC
  • Place of OriginChina
  • PortShanghai China
  • Supply Ability1000 Tons Per Month
  • Payment TermsT/T, L/C,
  • More Less
    Description
    Description

    Application: 

    FEJ90, FEJ105, FEJ125 and FEJ150 are irradiation cross-linkable insulation compounds for wire and cables, which regards polyolefin resin

    as the basic raw material, and adds anti-oxidant, cross-linkable agent and modified agents and other additives. They have excellent extruding

    property and physical property and can be widely used for various control cables, instrument installment wires of automotive low-voltage wires,

    and electrical wires. The highest working temperature is 90-150℃. Moreover, they don’t contain heavy mentals like Pb, Ba, Cd, Cr, Sn and Sb,

    and all their properties can meet the requirements of ROHS Standard.

    Processing Indicator
    Recommend to use single-screw extruders with L/D= 20-25.

    Main technical data:

    Model

     

     

                    Machine Barrel Temperature 

                Molding Temperature

     

     

    FEJ90/FEJ105/FEJ125/FEJ150

     

    165℃-185℃

     

    185℃-195℃

                                   Item

     

    Unit

     

    Technical requirements

     

    FEJ90

    FEJ105

    FEJ125

    FEJ150

                              Tensile Strength

     

     

    Mpa

    ≥13.5

    ≥13.5

    ≥13.5

    ≥13.5

                            Elongation at Break

     

    %

    ≥350

    ≥350

    ≥350

    ≥350

                                     Density

     

    g/cm3

    <1

    <1

    <1

    <1

                            Dielectric Strength

     

    MV/m

    ≥25

    ≥25

    ≥25

    ≥25

                              Aging Condition

     

    /

    121

    ×168h

    136

    ×168h

    158

    ×168h

    180

    ×168h

    Tensile Strength Variation After Aging 

    %

    ±20

    ±20

    ±20

    ±20

    Elongation Variation After Aging 

    %

    ±20

    ±20

    ±20

    ±20

        Brittle Temperature With Low Temperature Impact

     

     

     

    ≤-76

     

    ≤-76

     

    ≤-76

     

    ≤-76

                           20 Volume Resistivity

     

     

    Ω.cm

    ≥1×1013

    ≥1×1013

    ≥1×1013

    ≥1×1013