TEWR125 is a kind of thermoplastic low-smoke halogen-free flame-retardant elastomeric compounds. The highest working temperature is 125℃. It has good mechanical property, electrical property, flame retardant property as well as processability.
  • ModelFEJW90/FEJW105/FEJW125/FEJW150
  • Brand NameEASTMAC
  • Place of OriginChina
  • PortShanghai
  • Supply Ability1000 Tons Per Month
  • Payment TermsL/C,T/T
  • More Less
    Description
    Description

    Application: 

    FEJW90, FEJW105, FEJW125, FEJW150 are irradiation cross-linkable low-smoke halogen-free insulation compounds, which don’t contain any

    heavy metals like Pb, Ba, Cd, Cr, Sn and Sb. Their properties can well meet RoHS Standard. They have good physical and mechanical properties,

    and are mainly used for the insulation of communication cables, control cables and power cables.

    Processing Indicator

    Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25. 

    Main technical data:

    Model

     

    Machine Barrel Temperature 

    Molding Temprature

     

    FEJW90/FEJW105/FEJW125/FEJW150

    130-140℃

     

    150-160℃

      

    Item

     

     

    Unit

     

    Specification

     

    FEJW90

    FEJW105

    FEJW125

    FEJW150

    Tensile Strength

     

    MPa

    ≥10

    ≥10

    ≥10

    ≥10

    Elongation at Break

     

    %

    ≥150

    ≥150

    ≥150

    ≥150

    Density

     

    g/cm3

    ≤1.5

    ≤1.5

    ≤1.45

    ≤1.45

    Dielectric Strength

     

    MV/m

    ≥20

    ≥20

    ≥20

    ≥20

    Aging Conditions

     

    /

    121×168h

    136×168h

    158×168h

    180×168h

    Tensile Strength Variation

    After Aging

     

     

    %

     

    ≥75

     

    ≥75

     

    ≥75

     

    ≥75

    Elongation Variation After Aging 

    %

    ≥75

    ≥75

    ≥75

    ≥75

    Brittle Temperature With Low

    Temperature Impact

     

     

     

    -40

     

    -40

     

    -40

     

    -40

    Volume Resistivity at 20 

    Ω·m

    ≥1.0×1012

    ≥1.0×1012

    ≥1.0×1012

    ≥1.0×1012

     

      

     